ZA25% ZA40% Fused Zirconia Alumina Supplier F8 F12 F14 F16 F20 F24 F30 Grain Zirconia Aluminum Oxide
ZA25% and ZA40% Fused Zirconia Alumina, also named Zirconia Aluminum Oxide grain, are premium fused abrasives produced by co-melting alumina and zirconia sand in electric arc furnaces. The two grades differ in zirconia content to satisfy varied grinding demands. Available grit sizes cover F8, F12, F14, F16, F20, F24 and F30, all coarse particles designed for heavy-duty grinding applications.
Benefiting from eutectic crystal structure, ZA grains feature excellent toughness and remarkable self-sharpening property. Under heavy mechanical load, micro-cracks develop to expose new sharp cutting edges, delivering high stock removal rate and long service life. ZA40% offers higher toughness than ZA25%, suitable for extreme heavy grinding on stainless steel and alloy steel. ZA25% provides cost-effective performance for general heavy metal processing.
These coarse grains are widely used for resin grinding wheels, flap discs and abrasive blasting. Strict quality control ensures stable grain size and low impurity. COA is available per batch. As a reliable supplier, we support customized packaging to meet abrasive manufacturers’ production needs.
TYPICAL CHEMICAL ANALISIS [%]
| Items | Al2O3 | ZrO2 | TiO2 | Fe2O3 | SiO2 |
| ZA25 | 68-72 | 24-30 | ≤1.5 | ≤0.5 | ≤1.0 |
| ZA40 | 55-57 | 35-44 | ≤1.5 | ≤0.5 | ≤1.0 |
PHYSICAL PROPERTIES
| Crystal Form | Monoclinic,tetragonal system |
| Reaction with acid and alkali | no |
| Reaction with carbon | Forming carbide since 1650C |
| Color | Grey |
| True Density | 4.20g/cm3 |
| Bulk Density | 2.18g/cm3 |
| Moh’s hardness | 9.0 |
| Knoop hardness | 1450-2000kg/cm2 |
| Melting point | 1900C |
| Maximum service temperature | 1700C |
| Specific heat capacity(cal/g.C) | 0.2205(50-500C) |
| Heat conductivity | 0.2718 cal/cm2.sec.C |
| Linear expansivity(X10-6) | 6.82(100-700C) |
PARTICLE SIZE DISTRIBUTION
| F4 | +8000um | 0 | +5600um | ≤20% | +4750um | ≥40% | +4750+4000um | ≥70% | -3350um | ≤3% |
| F5 | +6700um | 0 | +4750um | ≤20% | +4000um | ≥40% | +4000+3350um | ≥70% | -2800um | ≤3% |
| F6 | +5600um | 0 | +4000um | ≤20% | +3350um | ≥40% | +3350+2800um | ≥70% | -2360um | ≤3% |
| F7 | +4750um | 0 | +3350um | ≤20% | +2800um | ≥40% | +2800+2360um | ≥70% | -2000um | ≤3% |
| F8 | +4000um | 0 | +2800um | ≤20% | +2360um | ≥45% | +2360+2000um | ≥70% | -1700um | ≤3% |
| F10 | +3350um | 0 | +2360um | ≤20% | +2000um | ≥45% | +2000+1700um | ≥70% | -1400um | ≤3% |
| F12 | +2800um | 0 | +2000um | ≤20% | +1700um | ≥45% | +1700+1400um | ≥70% | -1180um | ≤3% |
| F14 | +2360um | 0 | +1700um | ≤20% | +1400um | ≥45% | +1400+1180um | ≥70% | -1000um | ≤3% |
| F16 | +2000um | 0 | +1400um | ≤20% | +1180um | ≥45% | +1180+1000um | ≥70% | -850um | ≤3% |
| F20 | +1700um | 0 | +1180um | ≤20% | +1000um | ≥45% | +1000+850um | ≥70% | -710um | ≤3% |
| F22 | +1400um | 0 | +1000um | ≤20% | +850um | ≥45% | +850+710um | ≥70% | -600um | ≤3% |
| F24 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500um | ≤3% |
| F30 | +1000um | 0 | +710um | ≤25% | +600um | ≥45% | +600+500um | ≥65% | -425um | ≤3% |
| F36 | +850um | 0 | +600um | ≤25% | +500um | ≥45% | +500+425um | ≥65% | -355um | ≤3% |
| F46 | +600um | 0 | +425um | ≤30% | +355um | ≥40% | 355+300um | ≥65% | -250um | ≤3% |
| F54 | +500um | 0 | +355um | ≤30% | +300um | ≥40% | +300+250um | ≥65% | -212um | ≤3% |
| F60 | +425um | 0 | +300um | ≤30% | +250um | ≥40% | 250+212um | ≥65% | -180um | ≤3% |
| F70 | +355um | 0 | +250um | ≤25% | +212um | ≥40% | +212+180um | ≥65% | -150um | ≤3% |
| F80 | +300um | 0 | +212um | ≤25% | +180um | ≥40% | +180+150um | ≥65% | -125um | ≤3% |
| F90 | +250um | 0 | +180um | ≤20% | +150um | ≥40% | +150+125um | ≥65% | -106um | ≤3% |
| F100 | +212um | 0 | +150um | ≤20% | +125um | ≥40% | +125+106um | ≥65% | -75um | ≤3% |
| F120 | +180um | 0 | +125um | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63um | ≤3% |
| F150 | +150um | 0 | +106um | ≤15% | +75um | ≥40% | +75+63um | ≥65% | -45um | ≤3% |
| F180 | +125um | 0 | +90um | ≤15% | +75um | * | +75+63um | ≥40% | -53um | * |
| F220 | +106um | 0 | +75um | ≤15% | +63um | * | +63+53um | ≥40% | -45um | * |
MAIN APPLICATIONS:
1.Making zircon fused alumina brick and building materials
2.Used for making bonded abrasives products,and process of grinding,sandblasting,surface treatment of metal products and other materials.
3.With good melt erosion resistance,Zirconia fused alumina has good grinding effect on steel,iron casting,heat resistant steel and other alloy materials.
4.Zirconia fused alumina can be made for heavy duty Zirconia fused alumina grinding wheel,snagging,cutting disc,Fiber disc,grinding rails,high speed abrasive belts etc
5.Used for making coated abrasives products,
6.Used for making lapping paste,polishing wax,emery cloth,sandpaper etc
- ZA is primarily used for steel conditioning wheels, snagging wheels, large diameter cut-offs and other grinding applications that require high speed and pressure. It’s also is recommended for refractories that require a high resistance to environmental corrosion and a low coefficient of thermal expansion. Applications include slide gates, glass tank refractories, and other applications requiring resistance to molten slags.