High Quality Factory Brown Fused Alumina Corundum Grit brown Corundum 12#-4000#Brown Fused Alumina Grit And Powder polishing and Sandblasting
Brown Fused Alumina Corundum Grit brown Corundum 12#-4000 is made from Calcined Bauxite. It is a hard and tough material, used in manufacturing of grinding wheels (both vitrified and resin bonded) and coated products. These grains are also used for shot blasting and as polishing media. Refractory grade BFA is used as a raw material in the manufacture of high alumina refractory..
PPHYSICAL PROPERTIES
| Specific Weight | 3.96 g/ cm3 |
| Mohs Hardness | 9.0 |
| Crystal form | α-Al2O3 |
| Melting Point | 2250℃ |
1.Used for refractory,casting,foundry and Painting etc
TTYPICAL CHEMICAL ANALISIS [%]
| Size | Al2O3 | Fe2O3 | SiO2 | TiO2 | CaO | MgO |
| 0-1mm 1-3mm 3-5mm 5-8mm | ≥95.0 | ≤0.30 | ≤1.0 | 1.7-3.4 | ≤0.42 | / |
| 200F 325F | ≥92.5 | ≤1.0 | ≤3.0 | 3.0-5.0 | ≤0.60 | / |
2,Used for abrasives,blasting,grinding,ceramic,rust removal,surface treatment, floor coating,abrasion resistant layer etc
TTYPICAL CHEMICAL ANALISIS [%]
| Al2O3 | Fe2O3 | SiO2 | MgO | CaO | TiO2 | Na2O | K2O | LOI |
| ≥95.0 | ≤0.30 | ≤1.0 | / | 0.42 | 1.7-3.4 | / | / | < 0.09 |
PPARTICLE SIZE DISTRIBUTION
| F8 | +4000um | 0 | +2800um | ≤20% | +2360um | ≥45% | +2360+2000um | ≥70% | -1700um | ≤3% |
| F10 | +3350um | 0 | +2360um | ≤20% | +2000um | ≥45% | +2000+1700um | ≥70% | -1400um | ≤3% |
| F12 | +2800um | 0 | +2000um | ≤20% | +1700um | ≥45% | +1700+1400um | ≥70% | -1180um | ≤3% |
| F14 | +2360um | 0 | +1700um | ≤20% | +1400um | ≥45% | +1400+1180um | ≥70% | -1000um | ≤3% |
| F16 | +2000um | 0 | +1400um | ≤20% | +1180um | ≥45% | +1180+1000um | ≥70% | -850um | ≤3% |
| F20 | +1700um | 0 | +1180um | ≤20% | +1000um | ≥45% | +1000+850um | ≥70% | -710um | ≤3% |
| F22 | +1400um | 0 | +1000um | ≤20% | +850um | ≥45% | +850+710um | ≥70% | -600um | ≤3% |
| F24 | +1180um | 0 | +850um | ≤25% | +710um | ≥45% | +710+600um | ≥65% | -500um | ≤3% |
| F30 | +1000um | 0 | +710um | ≤25% | +600um | ≥45% | +600+500um | ≥65% | -425um | ≤3% |
| F36 | +850um | 0 | +600um | ≤25% | +500um | ≥45% | +500+425um | ≥65% | -355um | ≤3% |
| F46 | +600um | 0 | +425um | ≤30% | +355um | ≥40% | 355+300um | ≥65% | -250um | ≤3% |
| F54 | +500um | 0 | +355um | ≤30% | +300um | ≥40% | +300+250um | ≥65% | -212um | ≤3% |
| F60 | +425um | 0 | +300um | ≤30% | +250um | ≥40% | 250+212um | ≥65% | -180um | ≤3% |
| F70 | +355um | 0 | +250um | ≤25% | +212um | ≥40% | +212+180um | ≥65% | -150um | ≤3% |
| F80 | +300um | 0 | +212um | ≤25% | +180um | ≥40% | +180+150um | ≥65% | -125um | ≤3% |
| F90 | +250um | 0 | +180um | ≤20% | +150um | ≥40% | +150+125um | ≥65% | -106um | ≤3% |
| F100 | +212um | 0 | +150um | ≤20% | +125um | ≥40% | +125+106um | ≥65% | -75um | ≤3% |
| F120 | +180um | 0 | +125um | ≤20% | ≥40% | ≥40% | +106+90um | ≥65% | -63um | ≤3% |
| F150 | +150um | 0 | +106um | ≤15% | +75um | ≥40% | +75+63um | ≥65% | -45um | ≤3% |
| F180 | +125um | 0 | +90um | ≤15% | +75um | * | +75+63um | ≥40% | -53um | * |
| F220 | +106um | 0 | +75um | ≤15% | +63um | * | +63+53um | ≥40% | -45um | * |
3.Used for Grinding,polishing,lapping,whetstone,polishing pads,ceramic membrance etc
TYPICAL CHEMICAL ANALISIS [%]
| Al2O3 | Fe2O3 | SiO2 | FeO | MgO | CaO | TiO2 | Na2O | K2O | LOI |
| 92.5-96.0 | ≤0.75 | ≤2.0 | / | ≤0.50 | / | 1.7-3.4 | / | / | < 0.09 |
APARTICLE SIZE DISTRIBUTION
CHAPTER Ⅰ（JIS STANDARD）
| Size | DO(um) | D3(um) | D50(um) | D94(um) |
| #240 | ≤127 | ≤103 | 57.0±3.0 | ≥40 |
| #280 | ≤112 | ≤87 | 48.0±3.0 | ≥33 |
| #320 | ≤98 | ≤74 | 40.0±2.5 | ≥27 |
| #360 | ≤86 | ≤66 | 35.0±2.0 | ≥23 |
| #400 | ≤75 | ≤58 | 30.0±2.0 | ≥20 |
| #500 | ≤63 | ≤50 | 25.0±2.0 | ≥16 |
| #600 | ≤53 | ≤41 | 20.0±1.5 | ≥13 |
| #700 | ≤45 | ≤37 | 17.0±1.5 | ≥11 |
| #800 | ≤38 | ≤31 | 14.0±1.0 | ≥9.0 |
| #1000 | ≤32 | ≤27 | 11.5±1.0 | ≥7.0 |
| #1200 | ≤27 | ≤23 | 9.5±0.8 | ≥5.5 |
| #1500 | ≤23 | ≤20 | 8.0±0.6 | ≥4.5 |
| #2000 | ≤19 | ≤17 | 6.7±0.6 | ≥4.0 |
CHAPTER Ⅱ（FEPA STANDARD）
| Size | D3(um) | D50(um) | D94（um) |
| F230 | ＜82 | 53.0±3.0 | >34 |
| F240 | ＜70 | 44.5±2.0 | >28 |
| F280 | ＜59 | 36.5±1.5 | >22 |
| F320 | ＜49 | 29.2±1.5 | >16.5 |
| F360 | ＜40 | 22.8±1.5 | >12 |
| F400 | ＜32 | 17.3±1.0 | >8 |
| F500 | ＜25 | 12.8±1.0 | >5 |
| F600 | ＜19 | 9.3±1.0 | >3 |
| F800 | ＜14 | 6.5±1.0 | >2 |
Mainly Applications
-Bonded Abrasives and Coated abrasives
-Refractory,casting,foundry,and painting etc
-Wet and dry blast media,grinding and polishing etc
-PCB plate(PCBA,FPC,LED) blasting
-Polishing wax,Grinding stones,polishing pads etc
-removal of scale, rust and old coatings
-ceramics shapes
-Grinding wheels,Cup wheels etc
-brake and friction linings